Coefficient of Thermal Expansion

The basis of CTE

Materials expand because an increase in temperature leads to greater thermal vibration of the atoms in a material, and hence to an increase in the average separation distance of adjacent atoms.

The linear coefficient of thermal expansion a (Greek letter alpha) describes by how much a material will expand for each degree of temperature increase, as given by the formula:

\[\alpha  = \frac{{dl}}{{l \times dT}}\]


dl = the change in length of material in the direction being measured
l = overall length of material in the direction being measured
dT = the change in temperature over which dl is measured

Although a ratio is dimensionless, expansion has the unit k−1, and is normally quoted in parts per million per °C rise in temperature. There is a related volume coefficient of thermal expansion, but the acronym CTE1 typically refers just to the linear expansion.

1 In some books you will find CTE referred to by the older (and less correct term) of TCE, or ‘Thermal (or Temperature) Coefficient of Expansion’.

[back to top]

CTE variation with materials

The magnitude of the CTE depends on the structure of the material. As can be visualised from Figure 1, the atoms would only stay at a constant separation at absolute zero; above that, their increasing thermal energy generates some movement about the mean, and the mean itself increases slightly because the bond energy curve has an asymmetric shape.

Figure 1: Plot of bonding energy against inter-atomic distance after Shackelford 1999

Figure 1: Plot of bonding energy against inter-atomic distance

Figure 1 also helps us to visualise why strongly-bonded insulators, such as ceramics have relatively low CTEs compared to metals, and why loosely-bonded structures such as polymers generally have high CTEs, especially those that are thermoplastics or elastomers.

Table 1 gives some examples of linear coefficients of thermal expansion for some of the materials we will be considering throughout this course.

Table 1: CTEs for some common electronic materials
material CTE (ppm/°C)
silicon 3.2
alumina 6–7
copper 16.7
tin-lead solder 27
E-glass 54
S-glass 16
epoxy resins 15–100
silicone resins 30–300

It is important to realise that:

[back to top]

Measuring CTE

With typical CTEs in the range 5-50 ppm/K, the changes in dimensions are extremely small. The proverbial ‘six-inch rule’, with a CTE of 11 ppm/K, will expand by only 1.65µm for each degree of temperature rise: this corresponds to only a few wavelengths of light. As such small changes in length are difficult to measure, early data tended to make measurements of the average CTE between two fixed temperatures, say 25°C and 300°C.

Although making accurate measurements is still beyond the scope of the average laboratory, CTEs are nowadays typically measured by interferometry, which looks at the changes in the interference pattern of monochromatic light, usually from a laser. You will find a description of this technique at

With this technique it is possible to plot strain against temperature throughout a heating or cooling cycle. The slope of the strain/temperature curve at a given temperature is the instantaneous coefficient of thermal expansion. Of course, to give comparisons with earlier figures, the average slope over a temperature range can also be derived from the data.

[back to top]

Implications for composite assemblies

It is tempting to think of such small CTE figures as meaningless for our purposes, until that is you remember the bimetallic strip experiment that you probably carried out at school. This uses a strip made of two different strips of metal, typically brass and steel, which are sandwiched together. Though straight at the temperature at which they were joined together (usually room temperature) the strip bends quite dramatically when place in a flame or in a dewar flask of liquid nitrogen, but returns to its rest state when the source of heat or cold is removed. This principle is used in applications such as cooker and fridge thermostats .

Most structures that you will design have materials with different CTEs sandwiched together or soldered/bolted on. When temperature excursions occur, because of changes in either ambient conditions or the power dissipated by the circuit, these materials will expand differently, leading to the creation of stresses. In severe cases, we may get warping of an entire board, or solder joint fracture. These are issues to which we will return in Failure mechanisms.

Self Assessment Questions

A double-sided FR-4 laminate 30cm long consists of a sandwich of epoxy, reinforced by woven fibres of E-glass, between two thin sheets of copper. Estimate the difference in length of foils and core when the laminate is 50°C hotter.

What stresses are set up? How might these be relieved? And what might happen if the copper were patterned?

go to solution